| Name |
Charakteristics |
Form
of delivery |
Viscosity
DIN EN ISO 3219
23 ºC |
recomm.
Quantity of
Hardener |
H-Active
Equivalent-
mass |
Gardner
Colour Index
ISO 4630 |
Temp.
Increase
23ºC > 40ºC |
Properties
and
Fields of
Application |
|
|
|
app.
[mPas] |
[g]
2) |
[g/Eq.] |
|
app.
[min] 1) |
|
| 1015
NF H |
modified
aliphatic polyamine |
100%,
flüssig |
250 |
81 |
140 |
<
7 |
18 |
flexibilised, hydrophobic, recktiv; coatings, levellers |
| 1065
H |
aliphatic
polyamineadduct |
100%,
flüssig |
1.200
(25°C) |
37 |
65 |
<
3 |
33 |
low
labeling due to low free amine content, adhesives/ primer for flooring |
| 1287-01
H |
modified
cycloaliphatic Polyamine |
100%,
flüssig |
100 |
50 |
87 |
<
2 |
23 |
low
viscous; for higly filled coatings, self-levelling and floor screed mortars
with good resistance |
| 1312
NF H |
modified
cycloaliphatic polyamineadduct |
100%,
flüssig |
450 |
66 |
115 |
<
2 |
26 |
superior
quality coatings and mortars with good resistance to chemicals |
| 1386
NF H |
modified
cycloaliphatic polyamineadduct |
100%,
flüssig |
150 |
49 |
85 |
<
2 |
13 |
reactive,
phenol-free hardener for coatings and self-levelling mortars with good
through-curing even at 5 °C |
| 1389
H |
modified
cycloaliphatic polyamine |
100%,
flüssig |
50 |
50 |
89 |
<
1 |
30 |
low
yellowing and low early watwerspotting for coloured quartz and levelling
screeds |
| 1393
NF H |
modified
cycloaliphatic polyamineadduct |
100%,
flüssig |
190 |
54 |
93 |
<
3 |
23 |
good standard adduct hardener with excellent general properties |
| 1410
NF H |
modified
heterocyclic polyamine |
100%,
flüssig |
550 |
50 |
95 |
<
6 |
6 |
fast
curing mortar coatings, adhesives, putties, tar-epoxy-systems |
| 1590
NF H |
modified
aliphatic polyamineadduct |
100%,
flüssig |
180 |
50 |
90 |
<
5 |
60 |
low viscosit, long potlife;
primer a. coatings for warm climate
|
| |
| 1) |
Temperature-increase from 23°C to 40 ºC /
100 ml Mixture (isol.) |
| 2) |
with 100 g CeTePox 152 R |
|